Leading Supplier of Stainless Steel 310
Specifications of Grade 310 Stainless Steel also equivalent to
SUS310 | SUS310s | 1.4845 | UNS 31008 | 1.4840 | 104845
Properties of SUS310 Stainless Steel
SUS310, combining excellent high temperature properties with good ductility and weldability, is designed for high temperature service. It resists oxidation in continuous service at temperatures up to 1150°C provided reducing sulphur gases are not present. It is also used for intermittent service at temperatures up to 1040°C.
SUS310S (UNS S31008) is used when the application environment involves moist corrodents in a temperature range lower than that which is normally considered “high temperature” service. The lower carbon content of SUS 310S does reduce its high temperature strength compared to SUS310.
Like other austenitic grades these have excellent toughness, even down to cryogenic temperatures, although other grades are normally used in this environment.
These properties are specified for flat rolled product (plate, sheet and coil) in ASTM A240/A240M. Similar but not necessarily identical properties are specified for other products such as pipe and bar in their respective specifications.
Chemical Formula of SUS 310 Stainless Steel
Fe <0.25% C | 24-26% Cr | 19-22% Ni | <2% Mn | <1.5% Si | <0.45% P | <0.3% S
Mechanical Properties of SS310 Stainless Steel
|Grade||Tensile Strength (MPa) min||Yield StrengElongation (% in 50mm) minh 0.2% Proof (MPa) min||Elongation (% in 50mm) min||Hardness (Rockwell B (HR B) max||Hardness (Brinell (HB) max|
Physical Properties of SS 310 Stainless Steel
|Grade||Density (kg/m3)||Elastic Modulus (GPa)||Mean Coefficient of Thermal Expansion (mm/m/°C)||Thermal Conductivity (W/m.K)||Specific Heat 0-100°C (J/kg.K)||Electrical Resistivity (nW.m)|
|0-100°C||0-315°C||0-538°C||at 100°C||at 500°C|
Corrosion Resistance of 310 Grade Stainless Steel
The high chromium content – intended to increase high-temperature properties – also gives these grades good aqueous corrosion resistance.
The PRE is approximately 25, and seawater resistance about 22°C, similar to that of Grade 316. Excellent resistance at normal temperatures, and when in high-temperature service exhibits good resistance to oxidising and carburising atmospheres. Resists fuming nitric acid at room temperature and fused nitrates up to 425°C.
Subject to stress corrosion cracking but more resistant than Stainless Steel Grades 304 (SUS304) or Stainless Steel Grades 316 (SUS316).
Heat Resistance of Grade 310 Stainless Steel
Good resistance to oxidation in intermittent service in air at temperatures up to 1040°C and 1150°C in continuous service. Good resistance to thermal fatigue and cyclic heating. Widely used where sulphur dioxide gas is encountered at elevated temperatures. Continuous use in 425-860°C range not recommended due to carbide precipitation, if subsequent aqueous corrosion resistance is needed, but often performs well in temperatures fluctuating above and below this range.
SUS310 is generally used at temperatures starting from about 800 or 900°C – above the temperatures at which SS304H and SS321 are effective.
Heat TreatmentSolution Treatment (Annealing) – heat to 1040-1150°C and cool rapidly for maximum corrosion resistance. This treatment is also recommended to restore ductility after each 1000 hours of service above 650°C, due to long term precipitation of brittle sigma phase.
* These grades cannot be hardened by thermal treatment.
Comparison of Type 310 Stainless Steel (SUS310)
|Grade||UNS No||Old British||Euronorm||Swedish SS||Japanese JIS|
Possible Alternative Grades to Grade 310 Stainless Steel
|Grade||Why it might be chosen instead of 310|
|3CR12||Heat resistance is needed, but only to about 600°C.|
|304H||Heat resistance is needed, but only to about 800°C.|
|321||Heat resistance is needed, but only to about 900°C. Subsequent aqueous corrosion resistance also required.|
|253MA (2111HTR)||A slightly higher temperature resistance is needed than can be provided by 310. Better resistance to reducing sulphide atmosphere needed. Higher immunity from sigma phase embrittlement is required.|
Technical Applications of UNS S31008 Stainless Steel
SUS310 Stainless Steel can be used in the following applications :
- Furnace parts
- Oil burner parts
- Carburising boxes
- Heat Treatment baskets and jigs
- Heat Exchangers
- Welding filler wire and electrodes
Our Sales and Supplier Network in SUS310/ SUS310s/ 310 Stainless Steel :
With over 15 years of experience and strong global sourcing networking in the market, we are proud to be the Stainless Steel Grade 310 Supplier and Exporter to :
- Australia, Pakistan, Malaysia, Singapore, Taiwan, China, Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, China, Sweden, United States, Dubai, Finland, Brunei, Germany.
Besides, we have the full range of Stainless Steel sheets, Stainless Steel Round Bar, Stainless Steel Rods, Stainless Steel Plate which consists of
– 300 Series Stainless Steel : SUS304, SUS304L, SUS309, SUS310, SUS316Ti, SUS317, SUS321, SUS347
– 400 Series Stainless Steel : SUS403, SUS410, SUS420, SUS431, SUS440C, SUS630, SUS904L
– Nitronic 30, Nitronic 50, Nitronic 60
– Super Duplex S32750, S32760